In this study, the potential for biogas production from biodegradable bioplastics was evaluated. Mater-Bi® (a family of maizestarch
based flexible films) and PLA (PolyLactic Acid; a rigid, polylactide-based, polymer) bioplastics were digested in laboratory
batch reactors, alone or in co-digestion with pig slurry or scotta (partially deproteinized cheese whey), at 35°C or 55°C. Methane
(CH4) and hydrogen (H2) production were monitored during the incubation period. Maximum CH4 (Mmax) or H2 (Hmax)
production per reactor, potential CH4 (BMP) or H2 (BHP) production g-1 volatile solids (VS), and residual VS in the digestates
were determined. Methane was produced when bioplastics were digested alone or with pig slurry, whereas H2 was produced only
in co-digestion with scotta. Mmax, BMP, Hmax and BHP were on average higher at 55°C than at 35°C (+69%, +158%, +51% and
+45%, respectively). At 35°C, in monodigestion, small amounts of CH4 (33 mL g-1 VS) were produced with Mater-Bi® only. At
55°C, the BMP for Mater-Bi® and for PLA were equal to 113 mL and 282 mL CH4 g-1 VS, respectively. Monodigestion of Mater-
Bi® and PLA at 55°C reduced the initial VS content by 51%. When PLA was in co-digestion with pig slurry, Mmax was 12%
higher than the theoretical one, with a synergistic effect. In co-digestion with scotta, a nearly significant 12% increase in H2
production was observed for Mater-Bi® incubated at 35°C. The exploitation of bioplastic waste in anaerobic digestion for biogas
production, together with or in alternative to conventional composting, appears a promising possibility for a successful waste
management.